Malaysian Journal of Chemistry, 2017, Vol. 20(1), 118 – 127

Characterisation of Crosslinks in Vulcanised Rubbers: From Simple to Advanced Techniques

K.L. Mok1 and A.H. Eng2*
1Malaysian Rubber Board, 148 Jalan Ampang, 50450 Kuala Lumpur, Malaysia
2Malaysian Institute of Chemistry (Institut Kimia Malaysia), 127 B, Jalan Aminuddin Baki, Taman Tun Dr Ismail,
60000 Kuala Lumpur, Malaysia
*Corresponding author: (e-mail: This email address is being protected from spambots. You need JavaScript enabled to view it.)

 Received: November 2017; Accepted: May 2018


Crosslink density is a valuable property that affects the functional performance of a vulcanized rubber. It is generally determined by the solvent swelling method. The presence of filler can affect the results of crosslink density determination. While the information on the total crosslink density is useful, when more than one type of crosslinks are present in a vulcanized rubber, further characterization work is necessary to understand the contribution of these crosslinks to the performance properties of the rubber. Therefore, the ionic and covalent crosslinks of carboxylated nitrile butadiene rubber and natural rubber can be quantified individually using solvents of different polarities. By using suitable chemical probes, such as thiolate ion, this technique also allows the separate determination of the mono- di- and polysulphidic crosslinks in vulcanized rubbers. The crosslink density can also be determined using the Mooney-Rivlin equation based on stress-strain data of vulcanized rubbers. By swelling vulcanized rubbers in styrene, polymerizing the styrene, and observing the microtomed rubbers under a transmission electron microscope, crosslinks that formed within a latex particle, or intra-particle crosslinks, and those of inter-particle crosslinks can be visualized and determined semi-quantitatively. This characterization technique is useful for one to understand the extent of inter-particle and intra-particle crosslinking reactions.

Key words: Rubber; types of crosslink; crosslink density; methods of determination; network visualisation


1. Grange, J. (2018) Functionalization of polyisoprene: towards the mimic of natural rubber, Ph.D. Thesis, University of Bordeaux, France.

2. Coran, A.Y. (2013) Vulcanization in the science and technology of rubber (4th edn.), The Science and Technology of Rubber (Fourth Edition), eds. J.E. Mark, B. Erman, and M. Roland, Elsevier B.V. Amsterdam, Netherlands.

3. Huggin, M.L. (1942) The viscosity of dilute solutions of long-chain molecules. IV. Dependence on concentration, J. Am. Chem. Soc., 64, 2716–2720.

4. Cragg, L. H., Manson, J. A. (1952) Normal and cross-linked polystyrene. II. Viscosity behaviour of polystyrene cross-linked in emulsion polymerization, J. Polym. Sci. Polym. Chem., 9, 265–278.

5. G. M. Bristow (1962) The Huggin’s k′ parameter for polyisoprenes, J. Polym. Sci., 62, S168–S171.

6. Eng, A.H., Ejiri, S., Kawahara, S. and Tanaka, Y. (1994) Structural characteristics of natural rubber: role of ester groups, J. Appl. Polym. Sci. Polym. Symp., 53, 5–14.

7. Eng, A.H., Kawahara, S. and Tanaka, Y. (1994) Trans-isoprene units in natural rubber, Rubber Chem. Technol., 67, 159-168

8. Mooney, M. (1940) A theory of large elastic deformation, J. Appl. Phys., 11, 582–592.

9. Kraus, G. (1963) Swelling of Filler-reinforced Vulcanisates, J. Appl. Polym. Sci., 7, 861–871.

10. Merckel, Y., Diani, J., Brieu, M. and Caillard, J. (2013) Effects of the amount of fillers and of the crosslink density on the mechanical behavior of carbon-black filled styrene butadiene rubbers, J. Appl. Polym. Sci., 129, 2086–2091.

11. Diani, J., Brieu, M., Gilormini, P. (2017) Effect of filler content and crosslink density on the mechanical properties of carbon-black filled SBRs, in Proceedings of the European Conference on Constitutive Models for Rubbers X, Munich, Germany, 2017, Chapter 1, 3–10.

12. Faridah, H.A.H., TIinker, A.J., and Farid, A.S. (2004) Determination of crosslink densities of filled rubbers by cyclic pre-straining, J. Rubb. Res., 7, 248–264.

13. Bandzierz, K., Reuvekamp, L., Dryzek, J., Dierkes, W., Blume, A. and Bielinski, D. (2016) Influence of network structure on glass transition temperature of elastomers, Materials., 9, 607–623.

14. South, J.T. (2001) Mechanical properties and durability of natural rubber compounds and composites, Ph.D Thesis, Virginia Polytechnic Institute and State University.

15. Lim, H.M., Vivayganathan, K. and Amir Hashim, M.Y. (2012) Properties of carboxylated nitrile latex film with varying thickness, J. Rubb. Res., 15, 167–178.

16. Campbell, D.S., Chapman, A.V., Goodchild, I.R. and Fulton, W.S. (1992) Experimental determination of the Mooney-Rivlin constant for natural rubber vulcanisates, J. nat. Rubb. Res., 7, 168–180.

17. Abdullah, A., Burfield, D. R. and Ong, E.L. (1985) Comparative resilience and differential scanning calorimetric studies of natural rubber vulcanisates, in Proc. Inter. Rubb. Conf. 1985, Kuala Lumpur, 83–94.

18. Mareanukroh, M., Hamed, G.R. and Eby, R.K. (1996) Fine scale characterization of crosslinking with the atomic force microscope, Rubb. Chem. Technol., 69, 801–806.

19. Kittipoomwong, P. and Pongprayoon, T. (2017) Degree of vulcanization of rubber latex by capillary viscometer, Key Eng. Mater., 728, 313–317.

back to top